UF Series
Features
- Neat (No Solvent)
- Low Modulus
- Broadly listed on chemical registrations worldwide
Properties Enabled
- Increased Flexibility
- Reduced Shrinkage
- Improved Adhesion
- High Transparency
Applications
- Elastomeric Materials
- Coatings
- Optical Materials
- Adhesives
- Inks
Properties
| Grade No. | UF-07DF | UF-C051 * | UF-C052 | UF-C053 | UF-C01 | UF-C012 | UF-0146 |
|---|---|---|---|---|---|---|---|
| Appearance | Liquid | Liquid | Liquid | Liquid | Liquid ~ Solid | Liquid | Liquid |
| Color (APHA) | 30 | 30 | 30 | 20 | – | 30 | 10 |
| Viscosity (Pa・s) | 27 [25℃] | 340 [25℃] | 14 [25℃] | 205 [25℃] | 15 [50℃] | 34 [50℃] | 50 [50℃] |
| Molecular Weight | 6,000 | 35,000 | 10,000 | 8,500 | 11,000 | 8,500 | 12,000 |
| Features | Low Tg | High elongation | Low viscosity | Low dielectric constant | Balance | Amorphous | Balance |
* UF-C051 requires a diluting solvent or diluting monomer when manufactured.
Regulations
| Grade No. | UF-07DF | UF-C051 | UF-C052 | UF-C053 | UF-C01 | UF-C012 | UF-0146 |
|---|---|---|---|---|---|---|---|
| Japan | Listed | Listed | Listed | Listed | Listed | Listed | Listed |
| Korea | Listed | Listed | Listed | Listed | Listed | Listed | Listed |
| Taiwan | Listed | Listed | Listed | Listed | Listed | Listed | Listed |
| China | Listed | Listed | Listed | Listed | Listed | Listed | Listed |
| U.S.A | Listed | Listed | Listed | Listed | Listed | Listed | Listed |
| Canada | Listed | Listed | Listed | Listed | Listed | Listed | Listed |
| Australia | Listed | Listed | Listed | Listed | Not Listed | Not Listed | Listed |
Coating Properties
| Grade No. | UF-07DF | UF-C051 | UF-C052 | UF-C053 | UF-C01 | UF-C012 | UF-0146 |
|---|---|---|---|---|---|---|---|
| Appearance | Clear | Clear | Clear | Clear | Clear | Clear | Clear |
| Elongation [%] | 82 | 210 | 96 | 44 | 84 | 85 | 75 |
| Strength [Mpa] | 2.4 | 0.9 | 1.2 | 1.0 | 4.0 | 4.4 | 20 |
| Elastic Modulus [Mpa/20℃] | 2.0 | 0.1 | 0.2 | 0.8 | 10 | 8 | 30 |
| Polymer Tg [℃] | -33 | -43 | -44 | -16 | 41 | -6 | 54 |
| Dielectric Constant | 3.35 | 3.03 | 3.06 | 2.93 | 3.66 | 3.25 | 3.40 |
| Curing Condition: | 1-hydroxycyclohexyl phenyl ketone 5 wt% added to the resin The integrated light quantity of ultraviolet irradiation is 600mj/cm2 |
| Thickness: | 100μm |
| Elongation・Strength: | Tensile Tester Temperature: 20~22℃, Tension Rate:10mm/min |
| Elastic modulus, Tg: | Dynamic Viscoelasticity Frequency: 1Hz, Rate of Temperature Increase: 5℃/min |
| Dielectric Constant: | Frequency: 1GHz |